Semi-Rebonded Magnesia Chrome Bricks
Semi-Rebonded Magnesia Chrome Bricks and Fused-Rebonded Magnesia Chrome Brikcs are made of fine or partially fused magnesia. Procedure includes refined selection of Ingredients, high-pressure molding, ultra-high temperature firing, high direct bonding rate, good particle bonding, high temperature volume stability, and high temperature strengthening. It’s widely used in RH, AOD, VOD and other refining equipment and non-ferrous smelting furnace, on the blowing furnace and on the refining furnace.
| Brand | Chemical Analysia (%) | Physical Property | Description | Application | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| SiO2 | Al2O3 | Fe2O3 | CaO | MgO | Cr2O3 | C.C.S (MPa) |
A.P. (%) |
B.D. (g/cm3) |
R.U.D. (℃) |
T.S.R. (1100℃Water Cooling) |
|||
| 20 | 1.2 | 1.8 | 57 | 20 | 50 | 16 | 3.20 | 1700 | High strength, corrosion resistance, erosion resistance, good slag resistance, thermal shock stability |
Firing zone in cement kiln, non-ferrous furnace,steel making EAF, converter, AOD, VOD, galsss kiln, refining ladle | |||
| 18 | 1.2 | 1.7 | 60 | 18 | 45 | 17 | 3.20 | 1700 | |||||
| 16 | 1.5 | 1.5 | 62 | 16 | 45 | 17 | 3.18 | 1700 | |||||
| 14 | 1.5 | 1.5 | 65 | 14 | 45 | 17 | 3.18 | 1700 | |||||