Fused-Rebonded Magnesia Chrome Brikcs
Fused-Rebonded Magnesia Chrome Brikcs are made of fine or partially fused magnesia. Procedure includes refined selection of Ingredients, high-pressure molding, ultra-high temperature firing, high direct bonding rate, good particle bonding, high temperature volume stability, and high temperature strengthening. It’s widely used in RH, AOD, VOD and other refining equipment and non-ferrous smelting furnace, on the blowing furnace and on the refining furnace.
| Brand | Chemical Analysia (%) | Physical Property | Description | Application | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| SiO2 | Al2O3 | Fe2O3 | CaO | MgO | Cr2O3 | C.C.S (MPa) |
A.P. (%) |
B.D. (g/cm3) |
R.U.D. (℃) |
T.S.R. (1100℃Water Cooling) |
|||
| 24 | 1.2 | 1.8 | 54 | 24 | 50 | 16 | 3.27 | 1700 | High strength, corrosion resistance, erosion resistance, excellent slag resistance, high temperature resistance | Non-ferrous furnace, EAF, converter, RH, AOD, VOD, galsss kiln, refining ladle | |||
| 20 | 1.2 | 1.5 | 58 | 20 | 45 | 16 | 3.25 | 1700 | |||||
| 18 | 1.5 | 1.5 | 60 | 18 | 45 | 16 | 3.20 | 1700 | |||||